Xometry.pro
en – UK
Knowledge & Community
Search
K
Quote & source your parts
Europe Europe
English Deutsch Français Italiano Español
Türkiye Türkiye
English Türkçe
United Kingdom United Kingdom
English
Global Global
English
select
navigate
switch tabs
Esc close

Get Instant Quote

Use our Instant Quoting Engine to easily quote and source your parts online

Get a Quote
Back
 Profile
Menu
Materials Library
Manufacturing Stories & Cases
Articles
E-Books & Guides
Free Tools
Webinars
Free Courses
Community Discussions
Create Topic
Quote & Source Your Parts
Get a Quote

Edit topic

Home Xometry Community Manufacturing Any experiences with plastic CNC machining (POM)?

Any experiences with plastic CNC machining (POM)?

0
M
4

Hello!

I’m planning to use CNC machining for plastic parts (Delrin/POM) for the first time and have typically worked with metals before. I’m considering the ‘as machined’ finish with a standard 3.2 µm surface roughness.

For those who have experience with plastic CNC machining, can ‘as machined’ parts generally be used as end parts, or do they often carry too many machining marks? Would it be better to choose a bead-blasted finish (or another type) to enhance the appearance? These early prototypes might be shown to our end customers, so they need to look reasonably good. Any tips or experiences would be very helpful.

Also, could anyone share some pictures of polymer parts you have produced using CNC machining? I’d appreciate it!

Thanks, Marcin

Link copied
Solved by Pierre-Yves Huet
Hello Marcin, Regarding the aspect, I would not recommend Bead blasting on this plastic material, because it will give a dull/grayer finish, which will be very noticeable if the material is black. The "as machined" aspect is generally appreciated for this material, and it can be specified on drawing to avoid machining marks, which leads to using a finishing milling step to keep the milling traces as small and discrete as possible. In my experience as support engineer, I can affirm that a lot of customers order parts in this material as an end part, without additional treatment or finish, but if the aspect is very important, you can specify a lower roughness, like Ra 1.6um, and indicate which surfaces should be ideally without tool marks. Best regards, Pierre-Yves
    • M

      Hello!

      I’m planning to use CNC machining for plastic parts (Delrin/POM) for the first time and have typically worked with metals before. I’m considering the ‘as machined’ finish with a standard 3.2 µm surface roughness.

      For those who have experience with plastic CNC machining, can ‘as machined’ parts generally be used as end parts, or do they often carry too many machining marks? Would it be better to choose a bead-blasted finish (or another type) to enhance the appearance? These early prototypes might be shown to our end customers, so they need to look reasonably good. Any tips or experiences would be very helpful.

      Also, could anyone share some pictures of polymer parts you have produced using CNC machining? I’d appreciate it!

      Thanks, Marcin

      0
      Reply
    • P
      Xometry Engineer

      Hello Marcin,
      Regarding the aspect, I would not recommend Bead blasting on this plastic material, because it will give a dull/grayer finish, which will be very noticeable if the material is black.

      The “as machined” aspect is generally appreciated for this material, and it can be specified on drawing to avoid machining marks, which leads to using a finishing milling step to keep the milling traces as small and discrete as possible.

      In my experience as support engineer, I can affirm that a lot of customers order parts in this material as an end part, without additional treatment or finish, but if the aspect is very important, you can specify a lower roughness, like Ra 1.6um, and indicate which surfaces should be ideally without tool marks.
      Best regards,
      Pierre-Yves

      0
      Reply
      Link copied
      • M
        Pierre-Yves Huet

        Thank you!

        0
        Reply
        Link copied
    • A

      What Mr Huet replied is accurate – I have similar experience. Here’s also a picture I just made of one of my recent ABS CNC machined parts, you can see that there are traces of milling, but they are not too visible. 

      0
      Reply
      Link copied
      • M
        AM_EngR

        Thank you for sharing, that looks good, indeed. Nice texture 🙂 

        0
        Reply
        Link copied
Any experiences with plastic CNC machining (POM)?
Your information:




Suggested Topics

Topic
Replies
Views
Activity
Material recommendation for axial guide replacement
Manufacturing
Hello everyone, I'm replacing a broken axial guide component from a spindle assembly—this part sits on the Z-axis and connects the drill to the mounted machine frame. It failed during a milling op, likely... read more
B
0
10
Jun 16
hidrogene turbine
Manufacturing
I want you to make me two hulls of about 20 cm radius and a 16 cm rotor for a turbine that will burn hydrogen with oxygen.
1
29
Jun 13
Best way to mount NEMA 17 motor on 2 mm aluminum base?
Manufacturing
I'm working on a compact test rig where I need to mount a NEMA 17 stepper motor onto a 2 mm thick aluminum sheet (EN AW-5754). The base has to stay as light as possible,... read more
T
r
2
67
Jun 03
Sheet metal hem
Manufacturing
Hello, I'm trying to create a hem on the edge of steel sheets between 200mm and 400mm long. I can't find any manufacturer in France who can perform such bending/rolling/shaping with a radius of... read more
s
P
1
66
May 23
Mesh accuracy concerns with FDM
Manufacturing
I'm working on a small gear-driven mechanism for a camera panning rig and considering printing the 45° bevel gears in PETG (FDM). Tooth pitch is 1.5 mm, and the gears will be rotating slowly... read more