Resistant material for small gear system

0
E
2

Looking for the best material for a locking mechanism for an electric vehicle charging connector. Essentially a small gear system that engages to prevent unplugging during charging. The gear teeth are low-load but need to resist wear from frequent cycles (5,000+ lock/unlock operations) and tolerate some outdoor exposure (moisture, temperature variation, occasional dirt). I’m weighing options between reinforced polymers (like PA6 with GF) and metal (like sintered steel or aluminum), but I’m concerned about balancing noise, lubrication, and longevity. Any advice?

    • E

      Looking for the best material for a locking mechanism for an electric vehicle charging connector. Essentially a small gear system that engages to prevent unplugging during charging. The gear teeth are low-load but need to resist wear from frequent cycles (5,000+ lock/unlock operations) and tolerate some outdoor exposure (moisture, temperature variation, occasional dirt). I’m weighing options between reinforced polymers (like PA6 with GF) and metal (like sintered steel or aluminum), but I’m concerned about balancing noise, lubrication, and longevity. Any advice?

      0
    • M

      I’ve gotta agree that a polymer is your best bet here. Something like aluminum may be too soft to resist wear of small gear teeth, and anything metallic is gonna need some lubrication and will have some rattling noise. There’s also expansion and contraction with outdoor temperature variations. With sintered steel, depending on the grade, corrosion with moisture may also be an issue.

      There are so many different options with polymers, especially since you’re not expecting high loads on the gears so you’ve gotta be able to find a good one. I think a modern engineered polymer will give you the longevity you’re looking for.

      0
      Reply
    • B

      When you say lubrication, I think immediately of nylon. Most grades are self-lubricating. Also, cost-wise, that should be cheaper than something metallic. So I think your suggestion of PA6 GF is a great one, and in fact, PA6 GF is commonly used for gears. You could consider slightly different grades, such as PA66 (but still with the additional glass fiber reinforcement). If you’re able to cast the gears, then cast PA6 (PA6 C) may also provide better mechanical properties due to its higher crystallinity.

      0
      Reply
Resistant material for small gear system
Your information:




Suggested Topics

Topic
Replies
Views
Activity
Best 3D printing material for child-safe educational toy prototype
Hello! I need advice on a small prototype for an educational toy aimed at children aged 3–6. It consists of interlocking geometric shapes (around 8–10 parts per set), with no mechanical function. I’m planning... read more
T
F
D
2
46
Jul 16
Alodine coating enough for avionics enclosures?
Hi there, my project is a CNC machined enclosure in 6061-T6 aluminum for an avionics module that’ll be mounted in a wing compartment exposed to temperature swings, some humidity, but not direct salt spray.... read more
G
j
R
2
59
Jul 15
Effect of zinc flake coating thickness on bolt performance
In an automotive subframe project using M12 class 10.9 bolts, exposed to salt spray and vibration, I’m looking into zinc flake coatings for corrosion protection. Curious if doubling the coating thickness—from 8 µm to... read more
B
n
T
2
141
Jun 26
direct metal laser sintering
I need to obtain hole/channel sizes of 0.65 mm. will this be obtainable with a 40-60 layer thickness in tool steel?
j
1
121
Jun 13
SLA material for outdoor indicator lenses
hi,  I'm recreating two small indicator lenses for a 1980s motorcycle restoration. These need to be clear, UV-stable, and able to handle exposure to sun and rain long-term. I’m planning to go with SLA... read more
R
R
V
2
273
Jun 24