Optimizing DMLS support structures for powder removal

0
E
1

Hi everyone, we’re looking to use DMLS to create intricate internal channels in a complex heat exchanger for a miniaturized cooling system in a portable medical device. Our main challenge is optimizing the design for both thermal efficiency and manufacturability. We’re aiming for a compact unit, approximately 100mm x 50mm x 30mm, with internal channels as small as 0.5mm in diameter. The material we’re considering is AlSi10Mg for its excellent thermal conductivity and corrosion resistance.

My specific question is about support structures for these internal channels. Given the complexity of our design, I’m concerned about powder removal post-printing. Has anyone here successfully implemented self-supporting geometries for similar small, intricate channels in DMLS? If so, what were your key design considerations to ensure proper powder evacuation while maintaining the structural integrity of the part?

Solved by Nikolaus Mroncz

Hey, hi, unsupported channels from 1 to 6mm are in general no problem. If it is smaller, like in your case, it could be challenging and there is no general answer possible and also it should be rated by seeing the whole design. You could also mail me directly under nmroncz@xometry.de

    • E

      Hi everyone, we’re looking to use DMLS to create intricate internal channels in a complex heat exchanger for a miniaturized cooling system in a portable medical device. Our main challenge is optimizing the design for both thermal efficiency and manufacturability. We’re aiming for a compact unit, approximately 100mm x 50mm x 30mm, with internal channels as small as 0.5mm in diameter. The material we’re considering is AlSi10Mg for its excellent thermal conductivity and corrosion resistance.

      My specific question is about support structures for these internal channels. Given the complexity of our design, I’m concerned about powder removal post-printing. Has anyone here successfully implemented self-supporting geometries for similar small, intricate channels in DMLS? If so, what were your key design considerations to ensure proper powder evacuation while maintaining the structural integrity of the part?

      0
    • Xometry Engineer

      Hey, hi, unsupported channels from 1 to 6mm are in general no problem. If it is smaller, like in your case, it could be challenging and there is no general answer possible and also it should be rated by seeing the whole design. You could also mail me directly under nmroncz@xometry.de

      0
      Reply
Optimizing DMLS support structures for powder removal
Your information:




Suggested Topics

Topic
Replies
Views
Activity
Cracking at snap-fit hook base in SLS PA12
Hello everyone, I'm using SLS 3D printing (PA12, 0.12 mm layer height) to create a snap-fit enclosure for a handheld sensor device. The enclosure has three internal hooks that flex about 1.5 mm during... read more
F
A
1
25
May 26
Choosing sheet metal thickness for a lightweight bracket
Hey, working on a small mounting bracket for a consumer electronics housing, cut and bent from stainless steel sheet (304 or 316). The part needs to stay under 200g, but it also has to... read more
D
M
1
42
May 23
Visibility of parting line on GF30 PA6 injection molded handle
Hello everyone, how visible can the parting line be on final molded parts? My team is currently designing a handle cover for an industrial machine, injection molded in PA6 with 30% glass fiber. Aesthetics... read more
T
C
1
62
May 06
Minimum embossed text size for TPU molding
Hey there, I'm designing a flexible watch strap that will be injection molded in TPU (Shore 85A). I want to include some small embossed text (branding and serial number) directly on the strap, but... read more
A
n
2
107
May 05
Printed bracket cracking – how to reinforce?
Hi,  I'm prototyping a small bracket for holding a plastic cover in place—roughly 60 × 30 × 10 mm, with two hooks and two screw holes (M3) on the top side. I printed it in PLA with 20% infill... read more
G
R
1
89
Apr 23