Xometry.pro
en – Global
Knowledge & Community
Search
K
Quote & source your parts
Europe Europe
English DeutschFrançaisItalianoEspañol
Türkiye Türkiye
English Türkçe
United Kingdom United Kingdom
English
Global Global
English
select
navigate
switch tabs
Esc close

Get Instant Quote

Use our Instant Quoting Engine to easily quote and source your parts online

Get a Quote
Back
 Profile
Menu
Materials Library
Manufacturing Stories & Cases
Articles
E-books & Guides
Free Tools
Webinars
Free Courses
Community Discussions
Create Topic
Quote & Source Your Parts
Get a Quote

Edit topic

Home Xometry Community Industrial Design Maximum safe draw depth for aluminum

Maximum safe draw depth for aluminum

0
E
6

Hi everyone, I’m designing an automotive underbody heat shield using 0.8 mm thick aluminum alloy 5052-H32 for progressive die stamping. My main challenge is determining the optimal draw depth for complex geometries without risking material thinning or tearing. Some areas of the part require a draw depth of up to 25 mm. Given the material properties and thickness, I’m concerned about maintaining part integrity during the deep drawing process. 

I’m looking for advice on:

  • Calculating the maximum safe draw depth for this specific material and thickness
  • Strategies to achieve deeper draws without compromising material integrity

Has anyone worked with similar geometries and materials? What approaches have you found successful in optimizing draw depth while ensuring part quality?

Link copied
Solved by Marshall

Hi,
To perform a basic check you can check the limiting draw ratio (LDR) using this formula: LDR =Dmax/d

Where Dmax is the maximum diameter of the blank and d is the diameter of the punch. You can determine the blank diameter using: r1 = r2(r2 + 2H)

Where r1 is the radius of the blank, r2 radius of the cup and H is the height of the cup. Once you have the blank radius you can calculate the LDR. Ultimately, you need to get the specific LDR for the material you are using from the material supplier. If your calculated LDR falls in the recommended range indicated by the supplier, then you should be able to deep draw the material. 

    • E

      Hi everyone, I’m designing an automotive underbody heat shield using 0.8 mm thick aluminum alloy 5052-H32 for progressive die stamping. My main challenge is determining the optimal draw depth for complex geometries without risking material thinning or tearing. Some areas of the part require a draw depth of up to 25 mm. Given the material properties and thickness, I’m concerned about maintaining part integrity during the deep drawing process. 

      I’m looking for advice on:

      • Calculating the maximum safe draw depth for this specific material and thickness
      • Strategies to achieve deeper draws without compromising material integrity

      Has anyone worked with similar geometries and materials? What approaches have you found successful in optimizing draw depth while ensuring part quality?

      0
      Reply
    • M

      Hi,
      To perform a basic check you can check the limiting draw ratio (LDR) using this formula: LDR =Dmax/d

      Where Dmax is the maximum diameter of the blank and d is the diameter of the punch. You can determine the blank diameter using: r1 = r2(r2 + 2H)

      Where r1 is the radius of the blank, r2 radius of the cup and H is the height of the cup. Once you have the blank radius you can calculate the LDR. Ultimately, you need to get the specific LDR for the material you are using from the material supplier. If your calculated LDR falls in the recommended range indicated by the supplier, then you should be able to deep draw the material. 

      0
      Reply
      Link copied
      • E
        Marshall

        Thank you Marshall, the calculation you provided seems to be for a cylindrical shape, how can I determine the max draw depth of more complex shapes?

        0
        Reply
        Link copied
      • M
        Esme Shaw

        The above equation was presented as a simple way to check if your material can be deep drawn. If it fails this check then it definitely won’t work for more complex shapes. For a more detailed analysis on a complex geometry, you will have to perform an FEA analysis. Alternatively, you can reach out to a deep drawing company as they will have more than enough experience to tell you if you can or cannot manufacture your part using your chosen material.

        0
        Reply
        Link copied
      • L
        Marshall

        As another user mentioned, you will not be able to do a simple hand calculation to check if your material can be deep-drawn. However, there are a few techniques that can reduce the possibility of failure when deep drawing difficult geometries. For example, lubrication, die design, and blank clamp pressure optimization can all help reduce common failure modes.

        0
        Reply
        Link copied
      • E
        Lloyd

        These interventions will all be in the control of the workshop manufacturing the part, is there anything I can do from a design or material selection perspective to improve formability?

        0
        Reply
        Link copied
      • L
        Esme Shaw

        Hi Esme, one thing I can think of is to use a softer material, for example, 5052-O, and then temper the completed part to 5050-H32.

        0
        Reply
        Link copied
Maximum safe draw depth for aluminum
Your information:




Suggested Topics

Topic
Replies
Views
Activity
Thermal expansion modelling for a braced rectangular steel tank
Industrial Design
hi, for a welded steel coolant reservoir for a test stand - 4 m × 2 m × 1.5 m with internal bracing I need to account for thermal expansion. Fluid runs at 80–90... read more
B
0
36
Dec 22
Designing holes for M3 threaded inserts in an ABS enclosure
Industrial Design
Hi! In my design for a small ABS enclosure for an onboard sensor module I want to switch from molded bosses to heat-set M3 inserts for the lid screws. Before I finalize CAD, what... read more
A
o
1
61
Dec 23
Airtight joint between two aluminum frame enclosures?
Industrial Design
Hi, I have two 400 mm cubical enclosures from 20×20 mm aluminum profiles with glass on all sides except one. I need to connect them into a single temperature-controlled unit and keep the joint... read more
M
F
1
131
Dec 12
SLA wall thickness issue for microfluidic channels
Industrial Design
Hi, I created a 3D design for a small microfluidic part using SLA (Clear Resin) with internal channels ~0.4 mm wide and wall thickness around 0.5 mm. The function relies on optical inspection through... read more
B
c
1
1.2k
Jul 29
Embossed vs. engraved text for outdoor molded parts
Industrial Design
Hi there, I need to add a part number and recycling symbol on the surface of molded parts in PP GF20 for outdoor use. I initially planned to use engraved text for aesthetic reasons,... read more
T
R
A
3
2.5k
Aug 08

Edit topic